Exaton 15W
Exaton 15W is a basic welding flux for submerged arc welding giving good slag removal and a fine bead appearance. Its relatively high basicity makes it suitable for joining of austenitic and duplex stainless steel when high impact strength is desired. Due to its low niobium content burn-off it can be used advantageously with stabilized wire electrodes. Exaton 15W is a high performance welding flux in many joining applications in the chemical, petrochemical and oil&gas industry. It is particularly suited for Exaton range of duplex wire electrodes (e.g. 22.8.3.L/25.10.4.L) due to the highly neutral behavior, which ensures an optimal balanced microstructure. Taking the benefit of its features (not limited to nice bead appearance and self slag release only), it can also be used in combination with NiCrMo-3 wire for several other applications (i.e. both joining and weld overlay).
Klasyfikacje
| Stopień, Gatunek, Kategoria | S A AF 2 |
| Nazwa | EN ISO 14174 |
Własności materiału spawalniczego
| Wskażnik zasadowości | nom: 1.9 |
| Gęstość | nom: 1.0 Kg/l |
| Typ żużlu | Fluoride basic CaF2-Al2O3-SiO2 |
| Prąd spawania | 1200 A (Using 60x0.5 mm strip) |
Zużycie topnika
| V | Zużycie topnika / 1 kg(2,2 lb) drutu DC+ |
| 26 V | 0.5 kg |
| 30 V | 0.6 kg |
| 34 V | 0.8 kg |
| 38 V | 1.0 kg |
| A | Wymiary | Prędkość jazdy |
| 580 A | 4.0 mm | 33 m/h |
Klasyfikacje
| Drut | AWS/EN |
| Exaton 19.9.Nb | A5.9:ER347/ 14343-A:S 19 9 Nb |
| Exaton Ni56 | A5.14:ERNiCrMo-4/ 18274:S Ni 6276 (NiCr15Mo16Fe6W4) |
| Exaton 25.10.4.L | A5.9:ER2594/ 14343-A:S 25 9 4 N L |
| Exaton Ni60 SAW | A5.14:ERNiCrMo-3/ 18274:S Ni 6625 (NiCr22Mo9Nb) |
| Exaton 19.12.3.L | A5.9:ER316L/ 14343-A:S 19 12 3 L |
| Exaton 19.9.L | A5.9:ER308L/ 14343-A:S 19 9 L |
| Exaton 20.25.5.LCu | A5.9:ER385/ 14343-A:S 20 25 5 Cu L |
| Exaton 22.15.3.L | A5.9:ER(309LMo)/ 14343-A:S 23 12 2 L |
| Exaton 22.8.3.L | A5.9:ER2209/ 14343-A:S 22 9 3 N L |
| Exaton 24.13.LHF | A5.9:ER309L/ 14343-A:S 23 12 L |
| Exaton 24.13.LNb | A5.9:ER”309LNb”/ 14343-A:S 23 12 Nb |
| Exaton 24.13.L | A5.9:ER309L/ 14343-A:S 23 12 L |
| Exaton 27.31.4.LCu | A5.9:ER383/ 14343-A:S 27 31 4 Cu L |
| Exaton 19.9.Nb HF | A5.9:ER347/ 14343-A:S 19 9 Nb |
| Exaton 22.12.HT | 14343-A:S 21 10 N |
| Exaton 25.22.2.LMn | A5.9:ER"310LMo"/ 14343-A:S 25 22 2 N L |
Dopuszczenia
| Drut | BV | DNV-GL | VdTÜV |
| Exaton 19.12.3.L | - | - | * |
| Exaton 19.9.L | - | - | * |
| Exaton 22.8.3.L | * | * | * |
| Exaton 25.10.4.L | * | * | * |
| *Potwierdzenia są uzależnione od lokalizacji zakładu produkcyjnego. W razie jakichkolwiek pytań prosimy o kontakt z firmą ESAB. |
Typowe właściwości mechaniczne
| Drut | Warunki | Granica plastyczności | Wytrzymałość na rozciąganie | Udarność KV | Wydłużenie względne |
| Exaton 19.12.3.L | Po spawaniu null | 390 MPa (57 ksi) |
530 MPa (77 ksi) |
100 J @ 20°C, (74 ft-lb @ 68 °F) 85 J @ -40°C, (63 ft-lb @ -40 °F) 40 J @ -196°C, (30 ft-lb @ -320.8 °F) |
41 % |
| Exaton 19.9.L | Po spawaniu null | 390 MPa (57 ksi) |
560 MPa (81 ksi) |
90 J @ 20°C, (67 ft-lb @ 68 °F) 35 J @ -196°C, (26 ft-lb @ -320.8 °F) |
35 % |
| Exaton 19.9.Nb | Po spawaniu null | 470 MPa (68 ksi) |
650 MPa (94 ksi) |
80 J @ 20°C, (59 ft-lb @ 68 °F) |
32 % |
| Exaton 19.9.Nb HF | Po spawaniu DC+ | 440 MPa (64 ksi) |
610 MPa (88 ksi) |
75 J @ 20°C, (56 ft-lb @ 68 °F) |
32 % |
| Exaton 20.25.5.LCu | Po spawaniu null | 345 MPa (50 ksi) |
550 MPa (80 ksi) |
125 J @ 20°C, (93 ft-lb @ 68 °F) 100 J @ -196°C, (74 ft-lb @ -320.8 °F) |
40 % |
| Exaton 22.12.HT | Po spawaniu null | 400 MPa (58 ksi) |
580 MPa (84 ksi) |
120 J @ 20°C, (89 ft-lb @ 68 °F) |
35 % |
| Exaton 22.15.3.L | Po spawaniu null | 400 MPa (58 ksi) |
600 MPa (87 ksi) |
140 J @ 20°C, (104 ft-lb @ 68 °F) |
40 % |
| Exaton 22.8.3.L | Po spawaniu null | 650 MPa (94 ksi) |
790 MPa (115 ksi) |
115 J @ 20°C, (85 ft-lb @ 68 °F) 85 J @ -40°C, (63 ft-lb @ -40 °F) |
33 % |
| Exaton 24.13.L | Po spawaniu null | 400 MPa (58 ksi) |
600 MPa (87 ksi) |
140 J @ 20°C, (104 ft-lb @ 68 °F) |
40 % |
| Exaton 24.13.LHF | Po spawaniu null | 410 MPa (59 ksi) |
600 MPa (87 ksi) |
140 J @ 20°C, (104 ft-lb @ 68 °F) |
40 % |
| Exaton 24.13.LNb | Po spawaniu null | 400 MPa (58 ksi) |
600 MPa (87 ksi) |
90 J @ 20°C, (67 ft-lb @ 68 °F) |
35 % |
| Exaton 25.10.4.L | Po spawaniu DC+ | 690 MPa (100 ksi) |
880 MPa (128 ksi) |
90 J @ 20°C, (67 ft-lb @ 68 °F) 60 J @ -40°C, (44 ft-lb @ -40 °F) |
25 % |
| Exaton 25.22.2.LMn | Po spawaniu DC+ | 335 MPa (49 ksi) |
575 MPa (83 ksi) |
120 J @ 20°C, (89 ft-lb @ 68 °F) |
42 % |
| Exaton 27.31.4.LCu | Po spawaniu null | 360 MPa (52 ksi) |
540 MPa (78 ksi) |
165 J @ 20°C, (122 ft-lb @ 68 °F) |
35 % |
| Exaton Ni56 | Po spawaniu HI 1.6-1.8 kJ/mm DC+ | 450 MPa (65 ksi) |
700 MPa (102 ksi) |
100 J @ -60°C, (74 ft-lb @ -76 °F) 80 J @ -196°C, (59 ft-lb @ -320.8 °F) 100 J @ -60°C, (59 ft-lb @ -320.8 °F) |
45 % |
| Exaton Ni60 SAW | Po spawaniu null | 445 MPa (65 ksi) |
715 MPa (104 ksi) |
93 J @ -60°C, (69 ft-lb @ -76 °F) 82 J @ -196°C, (61 ft-lb @ -320.8 °F) |
45 % |
Analiza stopiwa
| Typowy skład chemiczny stopiwa % | ||||||||||||||||||
| C | Co | Cr | Cu | FN WRC | FN WRC-92 | FN deLong | Fe | Mn | Mo | N | Nb | Nb+Ta | Ni | P | S | Si | V | W |
| Exaton 19.12.3.L | ||||||||||||||||||
| 0.01 % | - | 18.1 % | - | - | - | - | - | 1.5 % | 2.6 % | - % | - | - | 12.3 % | - % | - % | 0.5 % | - | - |
| Exaton 19.9.L | ||||||||||||||||||
| 0.02 % | 0.1 % | 19.5 % | 0.1 % | - | 6 % | - | - | 1.2 % | 0.15 % | 0.05 % | - | - | 10 % | 0.025 % | 0.012 % | 0.6 % | - | - |
| Exaton 19.9.Nb HF | ||||||||||||||||||
| 0.04 % | - | 19.4 % | 0.11 % | 12 % | - | 13 % | - | 1.4 % | 0.12 % | 0.04 % | 0.7 % | 0.7 % | 9.3 % | 0.02 % | 0.01 % | 0.66 % | - | - |
| Exaton 19.9.Nb | ||||||||||||||||||
| 0.03 % | 0.1 % | 18.7 % | 0.10 % | 5 % | - | 6 % | - | 0.9 % | 0.03 % | 0.05 % | 0.5 % | 0.6 % | 9.5 % | 0.018 % | 0.013 % | 0.5 % | - | - |
| Exaton 20.25.5.LCu | ||||||||||||||||||
| 0.01 % | - | 19.6 % | - % | - | - | - | - | 1.4 % | 4.5 % | - | - | - | 25 % | - % | - % | 0.5 % | - | - |
| Exaton 22.8.3.L | ||||||||||||||||||
| 0.01 % | - | 22.6 % | - | - | - | - | - | 1.2 % | 3.1 % | 0.15 % | - | - | 8.6 % | - % | - % | 0.7 % | - | - |
| Exaton 24.13.LNb | ||||||||||||||||||
| <=0.020 % | - | 23.5 % | - | - | - | - | - | 1.2 % | - | - | 0.7 % | - | 12 % | <=0.025 % | <=0.015 % | 0.7 % | - | - |
| Exaton 25.10.4.L | ||||||||||||||||||
| <=0.020 % | - | 24.5 % | - | - | - | - | - | 0.3 % | 4 % | 0.21 % | - | - | 9.6 % | <=0.020 % | <=0.015 % | 0.6 % | - | - |
| Exaton 25.22.2.LMn Current: DC+, 420A, 27V | ||||||||||||||||||
| 0.02 % | - | 24.5 % | 0.1 % | - | - | - | - | 4.0 % | 2.1 % | 0.12 % | - | - | 22.0 % | - | - | 0.1 % | - | - |
| Exaton 27.31.4.LCu | ||||||||||||||||||
| 0.01 % | - | 26.3 % | 1.0 % | - | - | - | - | 1.4 % | 3.5 % | 0.06 % | - | - | 31.3 % | 0.01 % | 0.003 % | 0.4 % | - | - |
| Exaton Ni56 DC+ | ||||||||||||||||||
| 0.01 % | 0.1 % | 15.1 % | - | - | - | - | 6.8 % | 0.4 % | 15.6 % | - | - | - | Bal % | - | - | 0.20 % | 0.1 % | 3.6 % |
| Exaton Ni60 SAW Current: DC+, 400A, 28V, travel speed: 25 m/h. | ||||||||||||||||||
| 0.02 % | - | 22 % | 0.1 % | - | - | - | 5 % | 0.2 % | 9 % | - | - | 3 % | - | 0.015 % | 0.005 % | 0.4 % | - | - |
Jak można zdobyć Exaton 15W
W równym stopniu zależy nam na przekazaniu urządzeń ESAB w ręce klientów, jak klientom na ich posiadaniu. Dlatego ich sprzedażą zajmują się dystrybutorzy, którzy poświęcają klientom pełną uwagę, zapewniają wsparcie i dostarczają należne korzyści. Dzięki ich fachowej wiedzy, klienci są w równym stopniu zadowoleni z procesu zakupu, jak z nabytego produktu.
Dla ułatwienia przygotowaliśmy także listę przeglądanych produktów. Odwiedzając naszą witrynę można klikać na dowolne produkty i dodawać je do tej listy. Po zakończeniu można ją wysłać do siebie lub wydrukować i zanieść do preferowanego dystrybutora.
Aby znaleźć dystrybutora firmy ESAB, wystarczy użyć lokalizatora dystrybutorów, który znajduje się na wszystkich stronach naszej witryny. Można także zadzwonić do obsługi klienta pod numer (32) 35 11 100, a my pomożemy podjąć właściwą decyzję.